超厚板TC4钛合金电子束焊接接头应力腐蚀敏感性

针对100 mm超厚板TC4钛合金电子束焊接接头，采用慢应变速率拉伸方法评价接头在人造海水中的应力腐蚀敏感性，分析接头的显微组织和断口形貌，对接头的腐蚀机制进行研究. 结果表明，室温条件下应变速率为ε=1×10-6 s-1时，母材在海水中未表现出应力腐蚀敏感性；焊缝上部、中部和下部具有轻微应力腐蚀敏感性. 焊缝在海水中发生阳极溶解，产生氢吸附，导致裂纹的萌生. 同时氢扩散诱导α'相界及α'相内发生位错塞积，进而使裂纹在更低的应力水平下发生扩展.     

A Study on Dual-Load-Zone Model of Overlying Strata and Evolution Law of Mining Stress

The changeable structure and movement law of overlying strata are the main contributor to the change of mining stress. Starting from the relevant theory of key stratum and particularly based on the theory of mine ground pressure and strata control, this research proposed a new solution to mining stress problems by establishing a dual-load-zone stratum structural model. Elastic foundation beam theory was used to solve the stress of overlying strata of the dual-load-zones with superposition method, which revised the traditional calculation method of mining stress. The abnormal increase of lead abutment pressure in the mining area was explained effectively, through which the evolution law of mining stress in the case of hard rock was obtained. The results indicate that mining stress experiences a drastic change within the range of 50 m ahead of the coal wall due to the collapse of main roof; under the influence of main key stratum and inferior key strata, the influence range of lead abutment pressure is extended up to approximately 120 m in the working face; this remarkable increase can be attributed to the excessive length of sagging zone. Results from both the dual-load-zone model experiment and field measurement demonstrate high consistency. The model can predict the influence range of abutment pressure effectively and thus guide the safety production of mining.     

Stress intensity factor evaluations for a curved crack in orthotropic particulate composites using an interaction integral method

This paper develops a domain-independent interaction integral (DII-integral) for extracting mixed-mode stress intensity factors (SIFs) for orthotropic materials with complex interfaces. The DII-integral does not require material property gradients, and moreover its validity is not affected by material interfaces. Combined with the extended finite element method (XFEM), the DII-integral is employed to investigate a straight crack in an orthotropic functionally graded plate and a curved crack in orthotropic particulate composites.     

Prenatal exposure to the fluoride containing psychiatric drug fluoxetine and anti-oxidative alterations in the neonatal rat brain

Fluoride is a key ingredient of many psychiatric drugs like fluoxetine (Prozac^®, Fluoxetine^®). Pregnant women frequently use this drug as they suffer from depression and anxiety disorders during this period. Fluoxetine is able to reach the fetus through the placenta and passes to the newborn through milk. In the present study, female Wistar rats were treated with 5, 10, and 20 mg/L fluoxetine (containing 94% fluorides) from pregnancy day 10 to day 20. After delivery, the levels of the enzymatic antioxidants in the brain of their offspring at postnatal day 2 were measured. The results showed that, in all fluoxetine exposed groups compared with the control group, there was a significant decrease (P < 0.01) in the glutathione, catalase, glutathione S-transferases and potassium and a non- significant increase (P > 0.05) in the activity of malondialdehyde and creatine kinase. The results suggest that fluoxetine may be a developmental neurotoxicant due to presence of fluoride hence must be used carefully during pregnancy.     

An experimental approach towards increasing mechanical durability of extruded fish feed in the drying process

Mechanical durability of extruded fish feed must be optimized to lower economic losses as well as emission of organic matter to aquatic environments. The glass transition hypothesis for viscoelastic biopolymers is demonstrated and confirmed experimentally to be valid for extruded fish feed pellets. It is proposed and demonstrated that it is important to avoid early glass transition onset, to optimize the obtained mechanical durability. From the proposed glass transition hypothesis, immediate process relevance to the pre-drying transport mechanism is demonstrated. Furthermore, measured mechanical durability is found to range from 1.5 to 5.0% loss, for different combinations of drying parameters.     

InSb红外探测器芯片粘接工艺研究

基于InSb红外探测器的封装特点,采用正交试验法研究了芯片粘接过程中基板平整度、粘接剂抽真空时间、配胶时间、固化条件等工艺参数对芯片性能及可靠性的影响。通过计算极差和方差分析了各因素对芯片可靠性的影响大小。结果表明,固化条件对粘接后芯片的性能影响最大,其次是配胶时间,而抽真空时间和基板平整度影响相对较小。针对极差分析得出的较优参数组合和较差参数组合,利用X射线衍射(XRD)研究了不同参数组合对晶片粘接的应力大小,所得结果与正交试验一致。     

高功率光纤激光器光纤器件封装应力影响研究

高功率激光器无源器件制作过程中封装不当引入的应力,会导致信号光光束质量劣化和光纤温升,为了解决此问题,理论分析了光纤形变对信号光模式分布的影响,利用有限元方法建立包层光导致光纤发热模型,实验研究了不同封装方式对光纤发热情况和信号光光束质量的影响。实验表明,应力导致的光纤形变会造成信号光M2值在受力方向上略微变小而其垂直方向上变大,在输出100 W信号光时,施加应力导致的M2值的变化最高为0.39,与仿真结果相符。在光纤温升方面,相比于使用硬质胶水带来的12 ℃温升,使用硅橡胶封装的剥离器将温升控制在5 ℃以内,且其封装应力引入的M2值的变化在0.05以内。     

非晶Fe粉掺杂Al-12Si合金的高温压缩变形行为

为提高Al-12Si合金的热变形抗力,并探索非晶Fe粉掺杂对Al-12Si合金热压缩行为的影响和掺杂非晶Fe粉热压缩中的晶化温度等,采用连续挤压技术制备了掺杂10wt%非晶Fe粉与不掺杂非晶Fe粉的Al-12Si合金试样,对试样进行了不同温度和应变速率下的热压缩试验,分析了试样在热压缩中的组织转变,以及采用双曲正弦关系构建了试样的热流变应力方程。结果表明:非晶Fe掺杂试样在450 ℃及以下的热压缩时,Fe维持非晶态,500 ℃时,则已发生晶化;掺杂10wt%非晶Fe粉使Al-12Si合金的热抗变形能力显著提高,其热压缩激活能Q=211.29 kJ/mol,比未掺杂非晶Fe粉的Al-12Si合金试样高40.78 kJ/mol,且热压缩过程中存在动态回复和动态再结晶;利用双曲正弦关系构建试样的热流变应力方程为ε·=4.42×10¹⁴[sinh(0.016 6σ)]^6.13exp(-211 290/RT),线性回归系数高达0.99,即可为非晶Fe粉掺杂试样的热加工提供一定的理论指导。